Starting materials: (PEA)2PbCl4 crystals, DMF, quartz substrates

Product: Thin film on quartz

Description: Dissolve the 2D single crystals into DMF at a concentration 6%∼10% relative to the total weight. Spin-coat at 3000 rpm for 30 s on quartz substrates. Anneal in air at 100 °C for 10 min before measurement.

Method: UV-Vis absorption

Description: Optical absorption spectra were obtained using a Shimadzu UV-3600 spectrophotometer.

K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.

Extraction method: Engauge Digitizer (Figure S3)
Entry added on: May 17, 2020, 12:06 p.m.
Entry added by: Xiaochen Du Duke University
Last updated on: March 30, 2022, 5:17 p.m.
Last updated by: Rayan C Duke University
Data correctness verified by:

• Rayan C Duke University

Starting materials: (PEA)2PbCl4 crystals, DMF, quartz substrates

Product: Thin film on quartz

Description: Dissolve the 2D single crystals into DMF at a concentration 6%∼10% relative to the total weight. Spin-coat at 3000 rpm for 30 s on quartz substrates. Anneal in air at 100 °C for 10 min before measurement.

Method: UV-Vis absorption

Description: Optical absorption spectra were obtained using a Shimadzu UV-3600 spectrophotometer.

K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.

Extraction method: Engauge Digitizer (Figure S3)
Entry added on: Oct. 26, 2021, 4:50 p.m.
Entry added by: Jannik Eisenlohr Michigan State University
Last updated on: March 30, 2022, 5:38 p.m.
Last updated by: Rayan C Duke University
Data correctness verified by:

• Rayan C Duke University