See all entries for this property (2 total)
Starting materials: PbI2, toluene, butyric acid, butylamine, formamidinium acetate
Product: Powder film on glass substrate
Description: PbI2, toluene, butyric acid, and butylamine were mixed in a capped flask. Separately, formamidinium acetate was dissolved in toluene and butyric acid. For this n=2 layered perovskite, the suspension was heated to 70 degrees Celsius and then cooled slowly, and the color changed from dark brown to red. The bright red is characteristic of this system. Centrifugation at 6000 rpm for three minutes was used to first isolate the solid, which was then re-dispersed in hexane and centrifuged again. This obtained the final paintlike paste solid. The paintlike paste was then deposited on a glass substrate. A Pasteur pipette was used to spread the paste over the surface and was then allowed to dry.
Method: Diffuse Reflectance Spectra
Description: Diffuse reflectance spectra were measured in a Shimadzu UV 2450 instrument. A Ba2SO4 powder palette was the reference used.
See all entries for this property (2 total)
Starting materials: PbI2, toluene, butyric acid, butylamine, formamidinium acetate
Product: Powder film on glass substrate
Description: PbI2, toluene, butyric acid, and butylamine were mixed in a capped flask. Separately, formamidinium acetate was dissolved in toluene and butyric acid. For this n=2 layered perovskite, the suspension was heated to 70 degrees Celsius and then cooled slowly, and the color changed from dark brown to red. The bright red is characteristic of this system. Centrifugation at 6000 rpm for three minutes was used to first isolate the solid, which was then re-dispersed in hexane and centrifuged again. This obtained the final paintlike paste solid. The paintlike paste was then deposited on a glass substrate. A Pasteur pipette was used to spread the paste over the surface and was then allowed to dry.
Method: Photoluminescence Spectra
Description: A Horiba-Jobin Yvon Fluorolog-3 instrument was used on the films to measure photoluminescence spectra. Excitation was perpendicular to the film and emission was collected at an angle of ~15 degrees. The data was corrected according to the lamp and detector details by using algorithms from the equipment software.