Starting materials: Acetonitrile, HI, Cl(CH2)2NH2, PbI2

Product: Thin film on glass substrate

Description: In 6:2:1 molar ratio HI, Cl-(CH2)2-NH2, and PbI2 were added to an acetonitrile solution. It was stirred for a short time at room temperature, forming a clear and yellow solution. It was then held at room temperature and allowed to evaporate, leaving behind crystals of the perovskite after a few hours. Thin films of the samples were prepared via spin-coating solutions of dissolved crystals in acetonitrile.

Method: UV-vis absorption

Description: A Lambda 19 Perkin-Elmer spectrometer using a Specac variable temperature cell P/N 21525 was used to directly measure the absorption spectra.

S. Sourisseau, N. Louvain, W. Bi, N. Mercier, D. Rondeau, F. Boucher, J. Buzaré, and C. Legein, Reduced Band Gap Hybrid Perovskites Resulting from Combined Hydrogen and Halogen Bonding at the Organic−Inorganic Interface, Chemistry of Materials 19, 600‑607 (2007). doi: 10.1021/cm062380e.

Extraction method: Engauge digitizer
Entry added on: July 13, 2020, 7:06 p.m.
Entry added by: Andrew Levin NREL