These data sets are directly related (linked) to each other

Photoluminescence peak position
Origin: experimental (T = 298.0 K)
Space group: P -1
Photoluminescence peak position

Crystal system: triclinic

Photoluminescence peak position, nm
Fixed parameters:
  • temperature = 298.0 K
K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.
System description
Dimensionality: D
Sample type: film
Related data
This data set is directly linked to other data sets: See all related data

Starting materials: (PEA)2PbI4 crystals, DMF, glass substrates

Product: Thin film on glass

Description: Dissolve the 2D single crystals into DMF at a concentration 6%∼10% relative to the total weight. Spin-coat at 3000 rpm for 30 s on quartz substrates. Anneal in air at 100 °C for 10 min before measurement.

Method: Photoluminescence

Description: The photoluminescence spectra were measured using a Horiba-Jobi-Yvon LabRAM ARAMIS system, with a 325 nm He-Cd laser excitation. The laser beam was collimated and focused through a 40X UV objective onto the sample surface at room temperature. Refer to figure 5.

K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.

Extraction method: Engauge Digitizer (Figure 5)
Entry added on: May 23, 2019, noon
Entry added by: Xiaochen Du Duke University
Last updated on: June 22, 2022, 10:09 p.m.
Last updated by: Rayan C Duke University
Data correctness verified by:
  • Rayan C Duke University

Download data
Data set ID: 381 Did you find any mistakes or inconsistencies about this data? Send us a note and we'll have a look at it and send you a reply. Thanks!

Photoluminescence

See all entries for this property (3 total)

Origin: experimental (T = 298.0 K)
Space group: P -1
K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.
System description
Dimensionality: D
Sample type: film
Related data
This data set is directly linked to other data sets: See all related data

Starting materials: (PEA)2PbI4 crystals, DMF, glass substrates

Product: Thin film on glass

Description: Dissolve the 2D single crystals into DMF at a concentration 6%∼10% relative to the total weight. Spin-coat at 3000 rpm for 30 s on glass substrates. Anneal in air at 100 °C for 10 min before measurement.

Method: Photoluminescence

Description: The photoluminescence spectra were measured using a Horiba-Jobi-Yvon LabRAM ARAMIS system, with a 325 nm He-Cd laser excitation. The laser beam was collimated and focused through a 40X UV objective onto the sample surface at room temperature. Refer to figure 5.

K. Du, Q. Tu, X. Zhang, Q. Han, J. Liu, S. Zauscher, and D. Mitzi, Two-Dimensional Lead(II) Halide-Based Hybrid Perovskites Templated by Acene Alkylamines: Crystal Structures, Optical Properties, and Piezoelectricity, Inorganic Chemistry 56, 9291‑9302 (2017). doi: 10.1021/acs.inorgchem.7b01094.

Extraction method: Engauge Digitizer (Figure 5)
Entry added on: March 14, 2019, 4:18 p.m.
Entry added by: Xiaochen Du Duke University
Last updated on: June 22, 2022, 9:35 p.m.
Last updated by: Rayan C Duke University
Data correctness verified by:
  • Rayan C Duke University

Download data
Data set ID: 9 Did you find any mistakes or inconsistencies about this data? Send us a note and we'll have a look at it and send you a reply. Thanks!


License

All data is available under the Creative Commons license with attribution clause, described here and, in its full text, here.