Crystal system: orthorhombic
| Band gap (optical, diffuse reflectance), eV |
|---|
Starting materials: PbI2, toluene, butyric acid, butylamine, butylammonium iodide
Product: Powder film on glass substrate
Description: PbI2, butyric acid, toluene, and butylamine were mixed in a capped flask. Separately, butylammonium iodide was dissolved in toluene with butylamine and butyric acid. The two solutions were combined and stirred until an insoluble yellow solid precipitated. The solid was removed by centrifuging at 6000 rpm for 3 minutes. The yellow solid was redispersed in toluene and centrifuged a second time, to produce the final products. The paintlike paste was then deposited on a glass substrate. A Pasteur pipette was used to spread the paste over the surface and was then allowed to dry.
Method: Diffuse reflectance spectra
Description: Diffuse reflectance spectra were measured in a Shimadzu UV 2450 instrument. A Ba2SO4 powder palette was the reference used. The reflectance was converted to absorbance.
See all entries for this property (3 total)
Starting materials: PbI2, toluene, butyric acid, butylamine, butylammonium iodide
Product: Powder film on glass substrate
Description: PbI2, butyric acid, toluene, and butylamine were mixed in a capped flask. Separately, butylammonium iodide was dissolved in toluene with butylamine and butyric acid. The two solutions were combined and stirred until an insoluble yellow solid precipitated. The solid was removed by centrifuging at 6000 rpm for 3 minutes. The yellow solid was redispersed in toluene and centrifuged a second time, to produce the final products. The paintlike paste was then deposited on a glass substrate. A Pasteur pipette was used to spread the paste over the surface and was then allowed to dry.
Method: Diffuse reflectance spectra
Description: Diffuse reflectance spectra were measured in a Shimadzu UV 2450 instrument. A Ba2SO4 powder palette was the reference used. The reflectance was converted to absorbance.